Lámina de techo española ASA 1050 envejecida con motas XR-S1050 de XROOF, especialista en láminas de PVC para techos. Solicite información.
Vintage ASA Spanish 1050 roof sheet with spot XR-S1050 from XROOF
XROOF offers a retro surface design appearance, designed to imitate the traditional roman and Spanish roofing tile in Europe-style roofs. Its inks spot color allows for the character of the roof tile to be visible, Provide a more three-dimensional roof design to make your roof more European-style architectural features. ASA Spanish 1050 roof sheet with spot XR-S1050 is Ideal for residential roofing or as a durable residential roofing and siding solution!INQUIRY
Durable Color
The surface material of XROOF ASA Spanish 1050 roof sheet with spot XR-S1050 is an imported ultra-high weather-resistant engineering resin, which has extraordinary weather resistance and can maintain its color stability.
Corrosion Resistance
XROOF ASA Spanish 1050 roof sheet with spot XR-S1050 has super weather resistance and anti-corrosion performance. ASA Spanish roof sheet is soaked in salt, alkali and various acids below 60% for 24 hours without chemical reaction. ASA spanish roof sheet is the preferred plastic roof sheet material for chemical industry areas and acid rain areas.
Waterproof Performance
XROOF ASA Spanish ink roof panel itself is dense and does not absorb water, and there is no microporous water seepage. ASA Spanish 1050 roof sheet is a one-piece roof tile design, and there are few overlapping positions during installation. Under the condition of correct installation, the waterproof performance of ASA Spanish 1050 roof sheet with spot XR-S1050 can be maximized.
Flame Resistance
XROOFASA Spanish 1050 roof sheet with spot XR-S1050 material belongs to flame-retardant material, which will be extinguished when it leaves the fire.
Insulation Performance
XROOF ASA Spanish 1050 roof sheet is an insulation roofing material product, and will remain intact in case of accidental discharge or thunderstorms.
ASA Spanish Roof Sheet Specification
Width: 1050mm
Effecived width: 960mm
Length: Customized
Thickness: 2.3mm, 2.5mm, 3.0mm
Application: Residential, Villas, Resorts, Hotels, Government Projects, etc.
ASA Spanish roof sheet is one of the most popular profiles in the XROOF product line, prized for its simple one-piece design, which exhibits a unique corrugated pattern on the roof surface.
Compared to clay roof tiles, Spanish colonial roof sheet can enhance almost any architectural style.
|
NO. |
Test item |
Test method |
Test condition |
Test result |
|
|
1 |
Xenon-arc Exposure |
ISO 4892-2:2013,ISO 105-A02:1993 Cor2: 2005 and ASTM D2244-11 |
ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH 18min light and water sparay Filter: Boro/Boro Exposure period: 500h |
Greyscale |
2-3 |
|
∆E*ab |
3.5 |
||||
|
2 |
Thermal resistance |
With reference to ASTM D3045-92(2010) and client’s requirements |
150℃.30min |
Visible deformation and color fading, but o other visible change. |
|
|
3 |
Muriatic acid resistance |
Medium: 35%(m/m) HCI(AR) Method: Immersion method Temperature: Room temperature Test time: 48h |
|||
|
4 |
Sulfuric acid resistance |
With reference to ISO 175-2010 and client’s requirements |
Medium: 30%(m/m) H2SO4(AR) Method: Immersion method Temperature: Room temperature Test time: 48h |
No visisble change |
|
|
5 |
Alikali resistance |
With reference to ISO 175-2010 and client’s requirements |
Medium: 40% (m/m) NaOH(AR) Method: Immersion method Temperature: Room temperature Test time: 48h |
No visible change. |
|
|
6 |
Density |
ISO 1183-1:2012 Method A |
Abosolute alcohol, 23±0.5℃ |
1.799g/cm3 |
|
|
7 |
Flexural strength |
ISO 178:2010/Amd.1:2013 Method A |
Specimen：100x10.96x3.12mm Testing speed: 1mm/min Span: 50mm |
41.3MPa |
|
|
8 |
Flexural modulus |
4520MPa |
|||
|
9 |
Charpy unnotched impact strength |
ISO 179-1: 2010 |
Specimen: ISO 179-1/1Eu Specimen thickness:3.13mm The capcaity of the pendulum: 5J Impact speed: 2.90m/s Span: 62mm
|
38Kj/M2 C(complete break) |
|
|
10 |
Vicat softening temperature |
ISO 306:2004 Method B50 |
Specimen thickness: 3.01mm Rate of temperature: 50℃/h |
77.3℃ |
|
|
11 |
Tensile strength |
ISO 527-1:2012 and ISO 527-2:2012 |
Specimen: Type 1B Specimen thickness:3.05mm Testing speed: 5mm/min Grip separation:115mm |
20.3MPa |
|
|
12 |
Nominal tensile strain at break |
13% |
|||
|
13 |
Impact resistance |
GB/T 8814-2004 Section 5.7 and 6.7 |
Precondition:-10℃，1h→ Take out and do test within 10s. Specimen thickness:3.02mm Geometry: H.25 Strike weight: 1.0kg Span: 200mm Number of specimens tested:10 |
Number of spcimen breakage:0 |
|
|
14 |
Dimensional change |
With reference to ASTM D1204-08 and client’s requirement |
Condition: 100℃，60min→ 23±2℃，50±5%RH,1h Specimen: 25x25cm Medium:Talcum powder |
X drection |
-0.7% |
|
Y direction |
-1.3% |
||||
|
15 |
Oxygen Index |
ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005 |
Specimen: Type III Specimen thickness: 3.2mm Ignition procedure: Method A |
32.8% |
|
|
16 |
Horizontal burning test |
UL 94-2013 Section 7 |
Specimen: 126x13.4x3.0mm Conditioning: 23±2℃ 50±5%RH,48h |
HB |
|
|
17 |
20mm Vertiacal burning test |
UL 94-2013 Section 8 |
Specimen: 126x13.4x3.0mm |
V-1 |
|
|
18 |
Burning test |
DIN 4102-1:1998-05 |
See appendix1 |
The sample tested met the requirements of class B2 |
|
Inquiry: Lámina de techo española ASA 1050 envejecida con motas XR-S1050 de XROOF
Related products
Lámina de teja Roma 1050 de ASA XR-R1050 de la marca XROOF | XROOF
Lámina de teja Roma 1050 de ASA XR-R1050 de la marca XROOF, especialista en láminas de PVC para techos. Consulte información.
Lámina de techo española ASA 1050 XR-S1050 de la marca XROOF de calidad
Lámina de techo española ASA 1050 XR-S1050 de la marca XROOF. Visite nuestra fábrica o consulte en línea.
Lámina de techo española de ASA con malla de fibra XR-S1050 de XROOF
Lámina de techo española de ASA con malla de fibra XR-S1050 de XROOF, especialista en láminas de PVC para techos. Solicite información.